《Table 1 Measured Tm3+concentrations in single crystals and molar fractions of Tm3+in starting mater
本系列图表出处文件名:随高清版一同展现
《Tm~(3+)掺杂Na_5Lu_9F_(32)单晶体的1.8μm优化发射性能研究(英文)》
The polished slices with various Tm3+doped concentrations were transparent as shown in Fig.1.The X-Ray Diffraction(XRD)was recorded by using a XD-98X diffractometer(XD-3,Beijing).The real Tm3+concentrations in single crystal weremeasured by an inductively coupled plasma atomic emission spectroscopy(ICP-AES PerkinElmerInc,Optima 3 000).Table 1lists the measured Tm3+concentrations and the molar fractions of Tm3+in raw material.A Cary 5 000 UV/VIS/NIR spectrophotometer was used for measurement of the absorption spectra.The emission spectra were recorded under the 790 nm LD excitation by a Triax 320 type spectrometer.The fluorescence lifetime at 1.86μm were recorded with FLSP920fluorescence spectrophotometer.All these measurements were carried out at room temperature.
图表编号 | XD0023374400 严禁用于非法目的 |
---|---|
绘制时间 | 2018.04.01 |
作者 | 盛启国、夏海平、汤庆阳、何仕楠、章践立、陈宝玖 |
绘制单位 | 宁波大学光电子功能材料重点实验室、宁波大学光电子功能材料重点实验室、宁波大学光电子功能材料重点实验室、宁波大学光电子功能材料重点实验室、宁波大学光电子功能材料重点实验室、大连海事大学物理系 |
更多格式 | 高清、无水印(增值服务) |
查看“Table 1 Measured Tm3+concentrations in single crystals and molar fractions of Tm3+in starting material”的人还看了
- Table 1.comparisons between the satellite-derived and in situ-measured netsr F, as well as each flux component, includin
- 表4 单晶涡轮叶片不同部位残余共晶相面积比Tab.4 Residual eutectic area ratios of single crystal turbine blade in different positions