《Table 1 Sintering conditions of each cermet sample》
提示:宽带有限、当前游客访问压缩模式
本系列图表出处文件名:随高清版一同展现
《"基于TiCN和(Ti,W,Ta)CN的混芯结构金属陶瓷冶金过程中物相、组织结构及力学性能演变(英文)"》
The nominal composition of cermets samples employed27wt%TWTCN-27wt%Ti CN-18wt%WC-9wt%Mo2C-4wt%Ta C-7.5wt%Co-7.5wt%Ni.The raw materials were ball milled withΦ10 mm WC-8Co alloy balls at a ball-to-powder mass ratio of 8:1 for 72 h.Here was shown in Fig.1 the SEM image and XRD pattern of ball milled raw materials.Then the cermets samples were obtained via pelletizing,compacting under a pressure of 120 MPa and finally sintering for 1.5 h.The sintering conditions were given in Table 1.